Introduction
HXFR-PC/ABS802 consists of environment friendly flame retardant system of bromine, passed the evaluation of SGS, CTI etc. certification authority and comply with EU ROHS requirement. Advantages: good compatibility with PC/ABS, high effective,high UV-Resistance, oxidative resistance, no mold corrosion, non-blooming, high smoothness and good low-temperature toughness.
Application
Mainly used in PC/ABS thin wall products and parts of computer, connecter, enclosure of notebook or mouse. Need add the toughening agent when using.
Index
Item |
Index |
Appearance |
White Granular |
Density g/cm3 |
1.95 |
Decomposition Temp ℃≥ |
300 |
Content %> |
88 |
Water Content %≤ |
0.1 |
Recommended Dosage |
100:10 |
Solubility Index g/min,200℃5kg |
80 |
Melting Temp ℃≥ |
140 |
Extrusion Process (Twin Screw Extruder)
Note: Vacuum when production; Recommended Screw L/D 1:36-40;
Packing/Storage
25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight.
Appendix:Application Examples
1-1.Formula
Materials |
Formula A |
Raw PC/ABS |
100 |
HXFR-PC/ABS802 |
10 |
1-2.Technical Data
Properties |
Test Methods |
Unit |
Raw Materials |
Formula A |
Density |
ASTM D-792 |
g/cm³ |
1.15 |
1.2 |
Melt Index(200℃5KG) |
ASTM D-955 |
g/10min |
- |
- |
Tensile Strength |
ASTM- D638 |
MPa |
54.2 |
54.9 |
Elongation At Break |
ASTM-D638 |
% |
38.2 |
22.2 |
Flexural Strength |
ASTM-D790 |
MPa |
70.2 |
72.3 |
Flexural Modulus |
ASTM-D790 |
MPa |
2054.5 |
2132.1 |
Izod Impact Strength Notched(23℃) |
ASTM-D256 |
KJ/m2 |
40.5 |
17.2 |
Flame Retardancy 3.2mm |
UL94 |
‐ |
Non flame retardant |
V0 |
GWFI |
IEC60695-2-12 |
750℃ |
‐ |
pass |
1-3. PC/ABS Injection Process:
Drying condition: Drying at 80-100 deg C to 2-3 hours by desiccant dryers.
Injection machine temperature setup:
Heating Zone |
Step1 |
Step2 |
Step3 |
Nozzle |
Temperature |
224 |
235 |
245 |
240 |
All the application typical data above are just for reference, not an official warranty certificate.Provide different design solutions according to requirement of customers.